日本出光PC G-2530---Injection molding, natural polycarbonate 30% glass fiber reinforced.
Enhanced tensile strength, dimensional stability, hardness and heat distortion resistance performance
G2530 物性表
物理性能额定值单位制测试方法
| 比重 | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| 收缩率 - 流动 | 0.15 到 0.60 | % | ASTM D955 |
| 吸水率 (23°C, 24 hr) | 0.11 | % | ASTM D570 |
硬度额定值单位制测试方法
| 洛氏硬度 (M 级) | 92 |
| ASTM D785 |
机械性能额定值单位制测试方法
| 拉伸模量 | 8100 | MPa | ASTM D638, ISO 527-2 |
| 抗张强度 (断裂) | 120 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 (断裂) | 3.0 | % | ASTM D638, ISO 527-2 |
| 弯曲模量 | 8530 | MPa | ASTM D790, ISO 178 |
| 弯曲强度 | 170 | MPa | ASTM D790, ISO 178 |
冲击性能额定值单位制测试方法
| 悬壁梁缺口冲击强度 (3.20 mm) | 160 | J/m | ASTM D256 |
热性能额定值单位制测试方法
| 载荷下热变形温度 (1.8 MPa, 未退火) | 144 | °C | ASTM D648, ISO 75-2/A |
| 线形热膨胀系数 - 流动 | 2.3E-5 | cm/cm/°C | ASTM D696 |
电气性能额定值单位制测试方法
| 体积电阻率 | 1.0E+16 | ohms·cm | ASTM D257 |
| 介电强度 (1.60 mm) | 22 | kV/mm | ASTM D149 |
| 介电常数 |
|
| ASTM D150 |
| 60 Hz | 3.10 |
| ASTM D150 |
| 1 MHz | 2.95 |
| ASTM D150 |
| 耗散因数 |
|
| ASTM D150 |
| 60 Hz | 8.0E-4 |
| ASTM D150 |
| 1 MHz | 9.0E-3 |
| ASTM D150 |
| 耐电弧性 | 110 | sec | ASTM D495 |
可燃性额定值单位制测试方法
| 热灯丝点火温度 (3.20 mm) | 960 | °C | IEC 60695-2-13 |