PPA HTV-5H1瑞士EMS----Remarks: it still has high strength and hardness at high temperature. The absorption of water has little influence on its characteristics, good dimensional stability and small warpage tendency, good chemical resistance, good surface of molded products and good production efficiency, so that the cost can be effectively utilized. 50% glass fiber reinforced
备注说明： 高温下仍具有高强度与硬度、水份的吸收对其特性影响甚小、尺寸稳定性佳且翘曲倾向小、抗化学性佳、成型品表面品质佳 、生产效率佳，使成本有效被利用。含50%的玻纤增强
HTV-5H1 物性表
| 吸湿率 | ASTM D-570 | ||
| (24hr) | 0.13 | % | |
| (73℉(23℃)/50%rh) | 1.50 | % | |
| (73℉(23℃)in water) | 4.00 | % |
| 比重 | 1.65 | ASTM D-792 | |
| 模压收缩率 | ASTM D-955 | ||
| 0.007 | In/in | ||
| 0.005 | In/in | ||
| 0.002 | In/in |
| 拉伸强度 (248℉(120℃)) | 29800(206) | Psi(MPa) | ASTM D-638 |
| 弯曲模量 (73℉(23℃)) | 2400000(16550) | Psi(MPa) | ASTM D-790 |
| 断裂伸长率 (73℉(23℃)) | 2 | % | ASTM D-638 |
| 挠曲强度 (73℉(23℃)) | 43500(300) | Psi(MPa) | ASTM D-790 |
| 缺口冲击强度 | 1.80(96) | Ft-lb/in(J/m) | ASTM D-256 |
| 挠曲强度 (248℉(120℃)) | 43500(300) | Psi(MPa) | ASTM D-790 |
| 硬度 | 93 | D-SCAL | |
| 拉伸强度 (73℉(23℃)) | 39800(206) | Psi(MPa) | ASTM D-638 |
| 弯曲模量 (248℉(120℃)) | 2400000(16550) | Psi(MPa) | ASTM D-790 |
| 介电强度 | |||
| 600 | Volts | ASTM D-3638 | |
| (3mm) | 35 | KV/in | DIN 53481 |
| 表面电阻率 | 10 | VDE 0303-3 | |
| 体积电阻率 | 10 | Ω.cm | DIN 53482 |
其他新闻
- PPA GV-2H瑞士EMS 2024-01-16
- PPA HTN51G15HSL美国杜邦 2024-01-16
- PPA GV-6H瑞士EMS 2024-01-16
- PPA GV-4H瑞士EMS 2024-01-16
- PPA AS-4133 L美国苏威 2024-01-16
- PPA HTN51G35HSL美国杜邦 2024-01-16
- PPA美国杜邦PPA FR52G30BL 2024-01-16
- PPA瑞士EMS PPA GV-5H 2024-01-16
- 192X TPU科思创 2024-01-16
- 9385 TPU科思创 2024-01-16
- 1185A10 TPU巴斯夫 2024-01-16
- 1180A TPU巴斯夫 2024-01-16
- 1170A TPU巴斯夫 2024-01-16
- 9370AU TPU科思创 2024-01-16
- TPU 385SX德国科思创 2024-01-16